采用激光分子束外延技术在Al2O3衬底上成功外延生长了ZnS薄膜.用X射线衍射、扫描电子显微镜和光致发光谱表征了衬底温度对薄膜结构、形貌和光学特性的影响.结果表明所生长的ZnS薄膜为闪锌矿,具有(111)择优长向,随衬底温度的升高,X射线衍射峰的半高宽先减小后增大,在衬底温度为300℃时,半高宽最窄.薄膜结构致密,表面不平整度随衬底温度的升高而增大.薄膜的带隙随衬底温度的升高出现蓝移,可见光区域透射率最高达到98;,在360 nm激发波长下,观测到402 nm和468 nm两个发光带,衬底温度为300℃时,发光最强.     

基于冲击光谱测量的氧化铝晶体高压相变诊断技术

氧化铝晶体是一种优良的光学透明窗口材料,更是地球内部的重要组成物质.利用气炮加载结合冲击光谱测量,不仅能够获得其发光特征,并且根据光谱分布特征得到高压结构相变信息.在自主搭建的冲击光谱动态测试平台上,结合多通道辐射高温计以及ICCD瞬态光谱测试技术在40~120 GPa的压力区间,研究了c切向氧化铝晶体的辐射发光效应.在可见光波段400~700 nm区间获得了氧化铝晶体的发光光谱和辐射温度结果,证实了光谱的结构特征和表观温度值与该压力下氧化铝的结构相变存在明显的关联性.     

Identifying the viscoelastic properties of soft matter from the indentation response of a hard film-soft substrate system

The indentation technique is widely used in measuring the mechanical properties of soft matter at the microscale or nanoscale,but still faces challenges by these unique properties as well as the consequent strong surface adhesion, including the strong nonlinear effect, unclear judgment of the contact point, difficulties in estimating the contact area, and the risk of the indenter piercing the sample. Here we propose a two-step method to solve these problems: lay a hard film on a soft matter, and obtain the viscoelastic properties of this soft matter through the indentation response of this composite structure. We first establish a theoretical indentation model of the hard film-soft substrate system based on the theory of plates, elastic-viscoelastic correspondence principle and Boltzmann superposition principle. To verify the correctness of this method, we measure the mechanical properties of the methyl vinyl silicone rubber(MVSR) covered by a Cu nanofilm. Finally, we test the effectiveness and error sensitivity of this method with the finite element method(FEM). The results show that our method can accurately measure the mechanical properties of soft matter, while effectively circumventing the problems of the traditional indentation technique.     

Simultaneous determination of cinnamaldehyde and its metabolite in rat tissues by gas chromatography–mass spectrometry

Cinnamaldehyde (CA), an active ingredient isolated from the traditional Chinese medicine Cortex Cinnamomi, has a wide range of bioactivities. To clarify the distribution characteristics of CA, a selective and sensitive method utilizing gas chromatography–mass spetrometry was initially developed for simultaneously determining the concentration of CA and its metabolite cinnamyl alcohol in rat tissues. Selected ion masses of m/z 131, 105 and 92 were chosen, and separation of the analytes was performed on a DB‐5 ms (30 m × 0.25 mm, 0.25 µm, thickness) capillary column by gas chromatography–mass spectrometry. The calibration curves demonstrated good linearity and reproducibility over the range of 20–2000 and 20–4000 ng/mL for various tissue samples. Recoveries ranged from 86.8 to 107.5%, while intra‐ and interday relative standard deviations were all <11.3%. The analysis method was successfully applied in tissue distribution studies for CA and cinnamyl alcohol. As CA and cinnamyl alcohol may inter‐convert to one another, simultaneous determination of both analytes provides a comparative and accurate data for tissue study. The concentrations of CA and cinnamyl alcohol remaining in spleen were the highest among the main organs, including heart, liver, spleen, lung, kidney and brain. In addition, there was no long‐term accumulation of CA in rat tissues. Copyright © 2014 John Wiley & Sons, Ltd.     

Preparation and gas sensing activity of La and Y co-doped titania nanoparticles

Journal of Sol-Gel Science and Technology - A novel gas sensing material, La–Y co-doped TiO2 nanoparticles, was synthesized by sol–gel method and applied to detect organic pollutants...     

中空介孔SiO2纳米球的制备、改性及其对Al3+荧光识别研究

中空介孔SiO2由于中空多孔的结构而常用作功能材料的基底.将中空介孔SiO2进行官能团修饰,并应用为荧光传感材料是中空介孔SiO2一个重要的研究领域.本论文采用聚丙烯酸(PAA)为中空模板,聚醚F127为造孔剂,正硅酸乙酯(TEOS)为硅源,氨水为催化剂在乙醇体系中制备了中空介孔SiO2纳米球.系统研究了搅拌速度和聚醚F127引入量对中空介孔SiO2纳米球形貌及比表面积的影响.通过透射电镜、N2-等温吸附脱附曲线等表征说明该合成方法具有很好的普适性,通过调节F127的引入可以实现对比表面积的有效控制.通过氨基化、席夫碱反应进行荧光修饰,进一步研究表明荧光修饰后的中空介孔SiO2纳米球在水溶液中能够实现对Al3+的有效检测,检测限为1.19×10 -7M.     

四方体MgO的制备及对有机染料的吸附

以六水氯化镁和六次甲基四胺为原料,采用水热法合成四方体MgO,考察其对有机染料甲基橙和亚甲基蓝的吸附行为.通过TGA-DTA、SEM、XRD、N2-sorption和FT-IR等手段表征样品.结果表明,原料浓度、温度和表面活性剂对四方体MgO结构的形成影响较小,而反应时间的延长有助于有序结构的组装.温度170℃、时间24h、MgCl2·6H2O与C6H12N4浓度比为1∶2和表面活性剂PVP是制备四方体MgO的最佳条件.在溶液浓度10mg · L-1的单一吸附实验过程中,四方体MgO对甲基橙和亚甲基蓝的去除率分别为91.3;和22.3;,吸附过程均为单层吸附且符合Langmuir等温吸附模型和伪二级吸附动力学方程.在溶液浓度40 mg·L-1、甲基橙和亚甲基蓝浓度比3∶1的混合溶液吸附过程中,四方体MgO对甲基橙和亚甲基蓝的去除率分别为80.1;和97.9;.     

减压扩散高阻密栅技术应用研究

本文对减压扩散机理及高阻密栅技术作了详细的分析,并就设备及工艺方面的关键技术进行了阐述,最后对减压扩散高方阻工艺及密栅匹配技术电池效率进行了对比分析,有以下结论:(1)减压扩散在工艺优化后,方阻均匀性得到大幅改善,达到3;以内.(2)减压扩散电池效率完全可达到常规产线的水平,且在高阻密栅方面更有优势,可有效提升太阳电池效率.     

烧结温度对煤系高岭土制备堇青石陶瓷的影响

我国的煤系高岭土具有明显的资源优势,应对其进行充分地研究和合理地应用,以缓和优质高岭土资源枯竭的燃眉之急.以鄂尔多斯煤系高岭土、鄂尔多斯滑石、工业氧化铝为原料,通过反应烧结一步合成堇青石,探讨了堇青石合成温度范围,以拓宽该煤系高岭土的应用范围.通过高温显微镜观察堇青石试样的合成温度范围为1400～1420℃.经1420℃合成的堇青石试样的吸水率为16.11;,显气孔率为28.44;,体积密度为1.77 g/cm3,径向烧成收缩为1.77;,厚度烧成收缩为4.80;,抗折强度为43.56 MPa.镁铝尖晶石是合成堇青石的重要中间产物,适当提高烧结温度可以促进镁铝尖晶石相向堇青石相转变,有利于堇青石晶粒的生长与发育.烧结温度的变化是堇青石晶粒发生变化的原因,同时导致液相量的变化,最终影响堇青石试样显微结构和烧结性能.